Verharding van precisiegietstukken

The solidification of precision castings is more important for castings. Generally, the solidification methods of castings are divided into two methods: layer-by-layer solidification and paste solidification according to the properties of metal materials; according to the structure of castings, they are divided into two methods: sequential solidification and simultaneous solidification. Here I would like to remind everyone that this layer-by-layer solidification and paste solidification are properties of materials, which are related to the solidification interval of metal materials, or the crystallization interval. The solidification region refers to the coexistence region of liquid-solid two phases in the molten metal; the so-called crystallization region is the temperature difference between the liquidus and the solidus of the molten metal. The temperature range determines how the alloy solidifies. This is the inherent property of the material. When the material is selected, its solidification method is also selected and determined. The latter two solidification methods have nothing to do with the metal material, and are mainly determined by the structure of the casting. In order to obtain a dense casting, according to the structure of the casting, find a way from the casting process to force the casting to adopt a certain solidification method. So, what does layer-by-layer solidification mean? As the name suggests, it is layer-by-layer solidification. That is to say, the solidification interval of the molten metal is a line. The solidification of pure metals or eutectic alloys crystallized at a constant temperature at a certain instant is layer-by-layer solidification. Simultaneous solidification, as the name implies, means that the entire casting is solidified at the same time. The solidification zone of the casting is very wide, and even during a certain period of solidification, the solidification zone runs through the entire section of the casting. So, what is sequential solidification and simultaneous solidification?

1. The so-called sequential solidification is to artificially change the sequence of solidification, so that the castings are solidified according to the process design requirements. Casting first, then gate, and finally riser, so that the shrinkage cavity in the casting is transferred to the riser, and then a dense casting is formed; at the same time, various methods are adopted for solidification to reduce the temperature difference of each part of the casting, so that each part of the casting is in the solidifies at the same time (regardless of its size and structure).

2. Sommige mensen begrijpen misschien dat het materiaal dat laag voor laag wordt gestold, het principe van sequentiële stolling moet aannemen; en het in pastavorm gestold materiaal moet het principe van gelijktijdige stolling aannemen. Is deze stelling juist? Nee! Dat is waar we het hierboven over hadden'. Laag-voor-laag stollen en pasteuze stollen zijn eigenschappen van het metalen materiaal zelf, en je hebt geen keus. Als de klant het gietmateriaal bepaalt, staat deze gelijk aan zijn beslissing. De sequentiële stolling en gelijktijdige stolling bepaalt u, de vakman. Ik weet niet of ik'ik dit duidelijk zeg, maar ik denk dat nogal wat mensen dit probleem door elkaar hebben gehaald, dus het is de moeite waard om het hier te herhalen. Met andere woorden, de gietstukken die zijn ontworpen met laag-voor-laag stollingsmaterialen kunnen het principe van gelijktijdige stolling volgens de structuur aannemen; terwijl de gietstukken die zijn ontworpen met papperige stollingsmaterialen het principe van sequentiële stolling kunnen aannemen.

3. Over het algemeen zijn grijs ijzer, koolstofarm staal, industrieel koper, aluminium, aluminium-siliciumlegeringen, enz. allemaal materialen die laag voor laag stollen. Het nodulair gietijzer, koolstofstaal, aluminium-koperlegering, aluminium-magnesiumlegering, magnesiumlegering, enz. behoren allemaal tot de pasta-stollingsmethode. Er is nog een probleem dat aandacht behoeft, namelijk het temperatuurverschil van de gietsectie of de temperatuurgradiënt. Wanneer de temperatuurgradiënt groot is, kan het pasta-achtige gestolde materiaal ook laag-voor-laag stollen.